Modified poly (ethylene oxide), is a high quality polymer modified additives derived from ethylene oxide-based polymer as the base material, modified by nano-technology to generate high-quality dry mortar additives, for the white ultra-fine powder for powder / dry mixed mortar system, excellent dispersion, and the minimal amount, significantly improve the mechanical properties of mortar / concrete, and special inorganic waterproof groups introduced, it has excellent water resistance, thickening the smooth sexual. 

 In the application of dry powder / dry mix mortar industry can significantly improve mortar performance, such as the flexibility of the mortar. Bond strength, crack resistance, scratch resistance, thixotropy, and organic / inorganic insulation sheet bonded force. Greatly enhance the cohesion of the mortar, adhesive force, a significant reduction in the use of latex powder, cellulose ether may also reduce the amount due to the optimization of the water retention properties, various types of inorganic cementitious materials, fillers, chemical additives has better compatibility. 

 Technical parameters 

 Exterior 
 White non-caking powder 

 Solid content 
 99 ± 1% 

 Degree of fineness 
 ≥ 100 mesh 

 Moisture content 
 ≤ 0.5% 

 PH value 
 5 to 9 



 Classification and use characteristics 

 Modified poly (ethylene oxide) can be divided into the following models: 5596,5596 H, 5077,5077 H, 5077T, 5077V, etc. 

 █ 5077 

 Universal: Suitable for plate bonding / clean surface, the crack resistance of the slurry system, ceramic tile adhesive / caulk, putty / plaster substrate. 

 Repair mortars, waterproof mortar, interface agents and masonry mortar 

 █ 5077H 

 Polystyrene particles slurry, glass beads slurry, perlite insulation slurry 

 █ 5077T 

 Enhanced with excellent resistance to freeze / weather resistance for a variety of special circumstances, for all parts of China under different climate, stable performance 

 For a variety of dry powder / dry mix mortar class 

 █ 5077V 

 Dedicated to the glass beads of paste, perlite thermal insulation, microcrystalline high-strength insulation, inorganic active thermal insulation 

 █ 5077N 
 Applicable to cement-based lightweight insulation material class 
 According to the special requirements of customers, we can debug you need a different model / type of modified poly (ethylene oxide) products. 

 Note: recommended, based on laboratory and user feedback conclusions, the actual use based on their own laboratory results, select 

 Modified poly (ethylene oxide) is a functional additives, with very good water resistance, bond strength and construction, the increase is relatively small, generally one ton plus 2-3kg, water resistance is very 

 , Coupled with good bond strength, bond strength at room temperature under the premise of low rubber powder dosage can be achieved, water-resistant adhesive force 

 Modified poly (ethylene oxide) and a good scrape, smooth construction, construction, surface smooth, bright, have good water resistance effect, the strength of a good one 

 Like the JG149-2003 standard products, insulation board binder, 2kg of modified poly (ethylene oxide) plus 6kg polymer powders can have a good bond strength, broken boards 

 Rate and water-resistant adhesive force, if taking into account the water resistance broken boards rate of 80% crumb rubber amount of raised to 12kg insulation board Plastering 2kg of modified poly (ethylene oxide), plus 13 - 

 15kg of latex powder, there is a very good bond strength. Water-resistant adhesive force, creased 

 In summary: 

 Bond in the amount of low rubber powder, high bond strength and water-resistant adhesive force 

 Plastering without waterproofing agent can get excellent waterproof adhesive force, breaking the board rate, water resistance, the brightness of the surface of the table 

 Modified polyethylene oxide, ethylene insulation mortar characteristics 

 We modified poly (ethylene oxide) the viscosity of the H-type investigation and the special requirements for the domestic market, we launched the updated modified poly (ethylene oxide) type H, with excellent 

 Bonding degree and a plasma effect, per ton of Powder and increase the amount of polyethylene oxide in 5-6kg modified H-premise, can easily achieve a 1:8 ratio, while the material has excellent 

 The leveling of differences, on the wall viscosity, adhesion, basically does not appear out material phenomenon in line with the JG158-2004 standard products 

 Add 4-modified poly (ethylene oxide) in the inorganic thermal insulation 12kg can completely replace the polymer powders and enhance the pulp scrape, constructability smooth, construction, surface 

 Smooth and bright, have good water resistance, while reducing the cellulose ether added usage, thereby improving the superiority of the slurry and the actual cost of materials to meet the 

 GB/T20473-2006 standard products 

 Other Description 

 Product information, technical data and precautions based on scientific knowledge as the basis of information provided at this stage in general, does not guarantee the relevance of the product under special conditions 

 Use, accuracy and reliability of the user for special purposes should be to choose the right products and construction methods, such as the need for more information or advice, please contact the company